FTC-ZS / Spray, 400 ml

Fast-drying surface and corrosion protection with outstanding long-term effect for metals

Advantages

• In the salt spray test in line with DIN 50021, coated metal parts displayed no corrosion, even after 500 hours.
• The high proportion of zinc in the dry film provides secure protection to all metal surfaces that are permanently exposed to the elements.
• Thanks to the adhesive layer of corrosion protection and the fact that it can be painted over, it is also ideal as a high-quality base layer.
• The high resistance to cracking and flaking of a metal base material was confirmed by the mandrel flex test in line with DIN EN ISO 1519 (without damage).

Functioning

• Dark-grey colour (similar to RAL 7042)
• Metal proportion of over 92% in dry film
• Shake can well for approx. 3 minutes
• Apply at a distance of 20–30 cm in a cross coat
• Surface dust-dry after just approx. 8 minutes *Fully hardened within 24 hours
• Smooth, non-porous film
• Abrasion-resistant
• Excellent corrosion protection with long-term effect
• Heat-resistant up to approx. 500 °C
• Electroconductive and suitable for spot welding
• Ideal processing temperature of 16 °C to 25 °C

Applications

• For all metals that need corrosion protection
• Rust protection base layer for surfaces threatened by water and weather
• For the coating of drilling and cutting points as well as welded joints
• Conductive interlayer for spot welding
• Repairing damaged zinc coatings

Building materials

• All iron and steel surfaces
• Blank laminations

You can find detailed information on building materials in the registration document.